High-temperature superconductivity

Unsolved problems in physics
What causes superconductivity at temperatures above 50 kelvin?

High-temperature superconductors (abbreviated high-Tc or HTS) are materials that have a superconducting transition temperature (Tc) above 30 K (−243.2 °C). From 1960 to 1980, 30 K was thought to be the highest theoretically possible Tc. The first high-Tc superconductor[1] was discovered in 1986 by IBM researchers Karl Müller and Johannes Bednorz, for which they were awarded the Nobel Prize in Physics in 1987.

Until Fe-based superconductors were discovered in 2008,[2][3] the term high-temperature superconductor was used interchangeably with cuprate superconductor for compounds such as bismuth strontium calcium copper oxide (BSCCO) and yttrium barium copper oxide (YBCO).

"High-temperature" has two common definitions in the context of superconductivity:

  1. Above the temperature of 30 K that had historically been taken as the upper limit allowed by BCS theory. This is also above the 1973 record of 23 K that had lasted until copper-oxide materials were discovered in 1986.
  2. Having a transition temperature that is a larger fraction of the Fermi temperature than for conventional superconductors such as elemental mercury or lead. This definition encompasses a wider variety of unconventional superconductors and is used in the context of theoretical models.

The label high-Tc may be reserved by some authors for those with critical temperature greater than the boiling point of liquid nitrogen (77 K or −196 °C). However, a number of materials - including the original discovery and recently discovered pnictide superconductors - had critical temperatures below 77K but are commonly referred to in publication as being in the high-Tc class.[4][5]

Technological applications benefit from both the higher critical temperature being above the boiling point of liquid nitrogen and also the higher critical magnetic field (and critical current density) at which superconductivity is destroyed. In magnet applications the high critical magnetic field may be more valuable than the high Tc itself. Some cuprates have an upper critical field around 100 teslas. However, cuprate materials are brittle ceramics which are expensive to manufacture and not easily turned into wires or other useful shapes.

Two decades of intense experimental and theoretical research, with over 100,000 published papers on the subject,[6] have discovered many common features in the properties of high-temperature superconductors,[7] but as of 2009, there is no widely accepted theory to explain their properties. Cuprate superconductors (and other unconventional superconductors) differ in many important ways from conventional superconductors, such as elemental mercury or lead, which are adequately explained by the BCS theory. There also has been much debate as to high-temperature superconductivity coexisting with magnetic ordering in YBCO,[8] iron-based superconductors, several ruthenocuprates and other exotic superconductors, and the search continues for other families of materials. HTS are Type-II superconductors, which allow magnetic fields to penetrate their interior in quantized units of flux, meaning that much higher magnetic fields are required to suppress superconductivity. The layered structure also gives a directional dependence to the magnetic field response.

Contents

History and progress

After more than twenty years of intensive research the origin of high-temperature superconductivity is still not clear, but it seems that instead of electron-phonon attraction mechanisms, as in conventional superconductivity, one is dealing with genuine electronic mechanisms (e.g. by antiferromagnetic correlations), and instead of s-wave pairing, d-waves are substantial.

One goal of all this research is room-temperature superconductivity.[16] However following numerous announcements of room-temperature superconductivity that were discredited on examination, most condensed matter physicists now treat with extreme skepticism any claims of this nature.

Examples

Examples of high-Tc cuprate superconductors include La1.85Ba0.15CuO4, and YBCO (Yttrium-Barium-Copper-Oxide), which is famous as the first material to achieve superconductivity above the boiling point of liquid nitrogen.

Transition temperatures of well-known superconductors (Boiling point of liquid nitrogen for comparison)
Transition temperature
(in kelvin)
Material Class
133 HgBa2Ca2Cu3Ox Copper-oxide superconductors
110 Bi2Sr2Ca2Cu3O10(BSCCO)
90 YBa2Cu3O7 (YBCO)
77 Boiling point of liquid nitrogen
55 SmFeAs(O,F) Iron-based superconductors
41 CeFeAs(O,F)
26 LaFeAs(O,F)
20 Boiling point of liquid hydrogen
18 Nb3Sn Metallic low-temperature superconductors
10 NbTi
9.2 Nb
4.2 Boiling point of liquid helium
4.2 Hg (mercury) Metallic low-temperature superconductors

Cuprates

Cuprate superconductors are generally considered to be quasi-two-dimensional materials with their superconducting properties determined by electrons moving within weakly coupled copper-oxide (CuO2) layers. Neighbouring layers containing ions such as lanthanum, barium, strontium, or other atoms act to stabilize the structure and dope electrons or holes onto the copper-oxide layers. The undoped 'parent' or 'mother' compounds are Mott insulators with long-range antiferromagnetic order at low enough temperature. Single band models are generally considered to be sufficient to describe the electronic properties.

The cuprate superconductors adopt a perovskite structure. The copper-oxide planes are checkerboard lattices with squares of O2− ions with a Cu2+ ion at the centre of each square. The unit cell is rotated by 45° from these squares. Chemical formulae of superconducting materials generally contain fractional numbers to describe the doping required for superconductivity. There are several families of cuprate superconductors and they can be categorized by the elements they contain and the number of adjacent copper-oxide layers in each superconducting block. For example, YBCO and BSCCO can alternatively be referred to as Y123 and Bi2201/Bi2212/Bi2223 depending on the number of layers in each superconducting block (n). The superconducting transition temperature has been found to peak at an optimal doping value (p =0.16) and an optimal number of layers in each superconducting block, typically n = 3.

Possible mechanisms for superconductivity in the cuprates are still the subject of considerable debate and further research. Certain aspects common to all materials have been identified.[7] Similarities between the antiferromagnetic low-temperature state of the undoped materials and the superconducting state that emerges upon doping, primarily the dx2-y2 orbital state of the Cu2+ ions, suggest that electron-electron interactions are more significant than electron-phonon interactions in cuprates – making the superconductivity unconventional. Recent work on the Fermi surface has shown that nesting occurs at four points in the antiferromagnetic Brillouin zone where spin waves exist and that the superconducting energy gap is larger at these points. The weak isotope effects observed for most cuprates contrast with conventional superconductors that are well described by BCS theory.

Similarities and differences in the properties of hole-doped and electron doped cuprates:

Iron-based superconductors

Iron-based superconductors contain layers of iron and a pnictogen—such as arsenic or phosphorus—or a chalcogen. This is currently the family with the second highest critical temperature, behind the cuprates. Interest in their superconducting properties began in 2006 with the discovery of superconductivity in LaFePO at 4 K[23] and gained much greater attention in 2008 after the analogous material LaFeAs(O,F)[14] was found to superconduct at up to 43 K under pressure.[15]

Since the original discoveries several families of iron-based superconductors have emerged:

Most undoped iron-based superconductors show a tetragonal-orthorhombic structural phase transition followed at lower temperature by magnetic ordering, similar to the cuprate superconductors.[21] However, they are poor metals rather than Mott insulators and have five bands at the Fermi surface rather than one. The phase diagram emerging as the iron-arsenide layers are doped is remarkably similar, with the superconducting phase close to or overlapping the magnetic phase. Strong evidence that the Tc value varies with the As-Fe-As bond angles has already emerged and shows that the optimal Tc value is obtained with undistorted FeAs4 tetrahedra.[31] The symmetry of the pairing wavefunction is still widely debated, but an extended s-wave scenario is currently favoured.

Other materials sometimes referred to as high-temperature superconductors

Magnesium diboride is occasionally referred to as a high-temperature superconductor because its Tc value of 39 K is above that historically expected for BCS superconductors. However, it is more generally regarded as the highest Tc conventional superconductor, the increased Tc resulting from two separate bands being present at the Fermi energy.

Fulleride superconductors[32] where alkali-metal atoms are intercalated into C60 molecules show superconductivity at temperatures of up to 38 K for Cs3C60.[33]

Some organic superconductors and heavy fermion compounds are considered to be high-temperature superconductors because of their high Tc values relative to their Fermi energy, despite the Tc values being lower than for many conventional superconductors. This description may relate better to common aspects of the superconducting mechanism than the superconducting properties.

Theoretical work by Neil Ashcroft in 1968 predicted that solid metallic hydrogen at extremely high pressure should become superconducting at approximately room-temperature because of its extremely high speed of sound and expected strong coupling between the conduction electrons and the lattice vibrations.[34] This prediction is yet to be experimentally verified.

All known high-Tc superconductors are Type-II superconductors. In contrast to Type-I superconductors, which expel all magnetic fields due to the Meissner effect, Type-II superconductors allow magnetic fields to penetrate their interior in quantized units of flux, creating "holes" or "tubes" of normal metallic regions in the superconducting bulk. Consequently, high-Tc superconductors can sustain much higher magnetic fields.

Ongoing research

The question of how superconductivity arises in high-temperature superconductors is one of the major unsolved problems of theoretical condensed matter physics. The mechanism that causes the electrons in these crystals to form pairs is not known.[7] Despite intensive research and many promising leads, an explanation has so far eluded scientists. One reason for this is that the materials in question are generally very complex, multi-layered crystals (for example, BSCCO), making theoretical modelling difficult.

Improving the quality and variety of samples also gives rise to considerable research, both with the aim of improved characterisation of the physical properties of existing compounds, and synthesizing new materials, often with the hope of increasing Tc. Technological research focuses on making HTS materials in sufficient quantities to make their use economically viable and optimizing their properties in relation to applications.

A cable containing Gadolinium has been demonstrated to carry 2800 A at 76 K. The cable has an outside diameter of 7.5mm and a bend radius of 12.5 cm.[35]

Possible mechanism

There have been two representative theories for HTS. Firstly, it has been suggested that the HTS emerges from antiferromagnetic spin fluctuations in a doped system.[36] According to this theory, the pairing wave function of the cuprate HTS should have a dx2-y2 symmetry. Thus, determining whether the pairing wave function has d-wave symmetry is essential to test the spin fluctuation mechanism. That is, if the HTS order parameter (pairing wave function) does not have d-wave symmetry, then a pairing mechanism related to spin fluctuations can be ruled out. (Similar arguments can be made for iron-based superconductors but the different material properties allow a different pairing symmetry.) Secondly, there was the interlayer coupling model, according to which a layered structure consisting of BCS-type (s-wave symmetry) superconductors can enhance the superconductivity by itself.[37] By introducing an additional tunnelling interaction between each layer, this model successfully explained the anisotropic symmetry of the order parameter as well as the emergence of the HTS. Thus, in order to solve this unsettled problem, there have been numerous experiments such as photoemission spectroscopy, NMR, specific heat measurements, etc. But, unfortunately, the results were ambiguous, some reports supported the d symmetry for the HTS whereas others supported the s symmetry. This muddy situation possibly originated from the indirect nature of the experimental evidence, as well as experimental issues such as sample quality, impurity scattering, twinning, etc.

Junction experiment supporting the d symmetry

There was a clever experimental design to overcome the muddy situation. An experiment based on flux quantization of a three-grain ring of YBa2Cu3O7 (YBCO) was proposed to test the symmetry of the order parameter in the HTS. The symmetry of the order parameter could best be probed at the junction interface as the Cooper pairs tunnel across a Josephson junction or weak link.[38] It was expected that a half-integer flux, that is, a spontaneous magnetization could only occur for a junction of d symmetry superconductors. But, even if the junction experiment is the strongest method to determine the symmetry of the HTS order parameter, the results have been ambiguous. J. R. Kirtley and C. C. Tsuei thought that the ambiguous results came from the defects inside the HTS, so that they designed an experiment where both clean limit (no defects) and dirty limit (maximal defects) were considered simultaneously.[39] In the experiment, the spontaneous magnetization was clearly observed in YBCO, which supported the d symmetry of the order parameter in YBCO. But, since YBCO is orthorhombic, it might inherently have an admixture of s symmetry. So, by tuning their technique further, they found that there was an admixture of s symmetry in YBCO within about 3%.[40] Also, they found that there was a pure dx2-y2 order parameter symmetry in the tetragonal Tl2Ba2CuO6.[41]

Qualitative explanation of the spin-fluctuation mechanism

While, despite all these years, the mechanism of high-Tc superconductivity is still highly controversial, this being due to mostly the lack of exact theoretical computations on such strongly interacting electron systems, most rigorous theoretical calculations, including phenomenological and diagrammatic approaches, converge on magnetic fluctuations as the pairing mechanism for these systems. The qualitative explanation is as follows.

In a superconductor, the flow of electrons cannot be resolved into individual electrons, but instead consists of many pairs of bound electrons, called Cooper pairs. In conventional superconductors, these pairs are formed when an electron moving through the material distorts the surrounding crystal lattice, which in turn attracts another electron and forms a bound pair. This is sometimes called the "water bed" effect. Each Cooper pair requires a certain minimum energy to be displaced, and if the thermal fluctuations in the crystal lattice are smaller than this energy the pair can flow without dissipating energy. This ability of the electrons to flow without resistance leads to superconductivity.

In a high-Tc superconductor, the mechanism is extremely similar to a conventional superconductor. Except, in this case, phonons virtually play no role and their role is replaced by spin-density waves. As all conventional superconductors are strong phonon systems, all high-Tc superconductors are strong spin-density wave systems, within close vicinity of a magnetic transition to, for example, an antiferromagnet. When an electron moves in a high-Tc superconductor, its spin creates a spin-density wave around it. This spin-density wave in turn causes a nearby electron to fall into the spin depression created by the first electron (water-bed effect again). Hence, again, a Cooper pair is formed. When the system temperature is lowered, more spin density waves and Cooper pairs are created, eventually leading to superconductivity. Note that in high-Tc systems, as these systems are magnetic systems due to the Coulomb interaction, there is a strong Coulomb repulsion between electrons. This Coulomb repulsion prevents pairing of the Cooper pairs on the same lattice site. The pairing of the electrons occur at near-neighbor lattice sites as a result. This is the so-called d-wave pairing, where the pairing state has a node (zero) at the origin.

See also

References

  1. ^ a b J. G. Bednorz, K. A. Mueller (1986). "Possible high TC superconductivity in the Ba-La-Cu-O system". Zeitschrift für Physik B 64 (2): 189–193. Bibcode 1986ZPhyB..64..189B. doi:10.1007/BF01303701. 
  2. ^ Iron Exposed as High-Temperature Superconductor: Scientific American
  3. ^ a b Z.-H. Ren et al. (2008). "Superconductivity and phase diagram in iron-based arsenic-oxides ReFeAsO1−δ (Re = rare-earth metal) without fluorine doping". EPL 83: 17002. Bibcode 2008EL.....8317002R. doi:10.1209/0295-5075/83/17002. 
  4. ^ http://www.stanford.edu/~tpd/research_hightc.html
  5. ^ http://physics.aps.org/articles/v1/21
  6. ^ M. Buchanan (2001). "Mind the pseudogap". Nature 409 (6816): 8–11. doi:10.1038/35051238. PMID 11343081. 
  7. ^ a b c A. Leggett (2006). "What DO we know about high Tc?". Nature Physics 2 (3): 134. Bibcode 2006NatPh...2..134L. doi:10.1038/nphys254. 
  8. ^ S. Sanna et al. (2004). "Nanoscopic Coexistence of Magnetism and Superconductivity in YBa2Cu3O6+x Detected by Muon Spin Rotation". Physical Review Letters 93 (20): 207001. arXiv:cond-mat/0403608. Bibcode 2004PhRvL..93t7001S. doi:10.1103/PhysRevLett.93.207001. 
  9. ^ K. M. Wu et al. (1987). "Superconductivity at 93 K in a new mixed-phase Y-Ba-Cu-O compound system at ambient pressure". Physical Review Letters 58 (9): 908–910. Bibcode 1987PhRvL..58..908W. doi:10.1103/PhysRevLett.58.908. PMID 10035069. 
  10. ^ H. Maeda, Y. Tanaka, M. Fukutumi, T. Asano (1988). "A New High-Tc Oxide Superconductor without a Rare Earth Element". Japanese Journal of Applied Physics 27: L209–L210. Bibcode 1988JaJAP..27L.209M. doi:10.1143/JJAP.27.L209. 
  11. ^ Z. Z. Sheng, A. M. Hermann (1988). "Bulk superconductivity at 120 K in the Tl–Ca/Ba–Cu–O system". Nature 332 (6160): 138–139. Bibcode 1988Natur.332..138S. doi:10.1038/332138a0. 
  12. ^ C. W. Chu et al. (1993). "Superconductivity above 150 K in HgBa2Ca2Cu3O8+δ at high pressures". Nature 365 (6444): 323. Bibcode 1993Natur.365..323C. doi:10.1038/365323a0. 
  13. ^ L. Gao. et al. (1994). "Superconductivity up to 164 K in HgBa2Cam-1CumO2m+2+δ (m=1, 2, and 3) under quasihydrostatic pressures". Physical Review B 50 (6): 4260–4263. Bibcode 1994PhRvB..50.4260G. doi:10.1103/PhysRevB.50.4260. 
  14. ^ a b Y. Kamihara, T. Watanabe, M. Hirano, and H. Hosono (2008). "Iron-Based Layered Superconductor La[O1-xFx]FeAs (x = 0.05−0.12) with Tc = 26 K". Journal of the American Chemical Society 130 (11): 3296–3297. doi:10.1021/ja800073m. PMID 18293989. 
  15. ^ a b H. Takahashi et al. (2008). "Superconductivity at 43 K in an iron-based layered compound LaO1-xFxFeAs". Nature 453 (7193): 376–378. Bibcode 2008Natur.453..376T. doi:10.1038/nature06972. PMID 18432191. 
  16. ^ A. Mourachkine (2004). Room-Temperature Superconductivity. Cambridge International Science Publishing. arXiv:cond-mat/0606187. ISBN 1904602274. 
  17. ^ C. Hartinger. "DFG FG 538 - Doping Dependence of Phase transitions and Ordering Phenomena in Cuprate Superconductors". Wmi.badw-muenchen.de. http://www.wmi.badw-muenchen.de/FG538/projects/P4_crystal_growth/index.htm. Retrieved 2009-10-29. 
  18. ^ H. Luetkens et al. (2009). "Electronic phase diagram of the LaO1-xFxFeAs superconductor". Nature Materials 8 (4): 305–9. Bibcode 2009NatMa...8..305L. doi:10.1038/nmat2397. PMID 19234445. 
  19. ^ A. J. Drew et al. (2009). "Coexistence of static magnetism and superconductivity in SmFeAsO1-xFx as revealed by muon spin rotation". Nature Materials 8 (4): 310–314. Bibcode 2009NatMa...8..310D. doi:10.1038/nmat2396. PMID 19234446. 
  20. ^ S. Sanna et al. (2009). "Competition between magnetism and superconductivity at the phase boundary of doped SmFeAsO pnictides". arXiv:0902.2156. 
  21. ^ a b J. Zhao et al. (2008). "Structural and magnetic phase diagram of CeFeAsO1-xFx and its relation to high-temperature superconductivity". Nature Materials 7 (12): 953–959. Bibcode 2008NatMa...7..953Z. doi:10.1038/nmat2315. PMID 18953342. 
  22. ^ J.-H. Chu, J. G. Analytis, C. Kucharczyk, I. R. Fisher (2008). "Determination of the phase diagram of the electron doped superconductor Ba(Fe1-x}Cox)2As2". arXiv:0811.2463. 
  23. ^ Y. Kamihara et al. (2006). "Iron-Based Layered Superconductor: LaOFeP". Journal of the American Chemical Society 128 (31): 10012–10013. doi:10.1021/ja063355c. PMID 16881620. 
  24. ^ G. Wu et al. (2009). "Superconductivity at 56 K in Samarium-doped SrFeAsF". Journal of Physics: Condensed Matter 21 (3): 142203. arXiv:0811.0761. Bibcode 2009JPCM...21n2203W. doi:10.1088/0953-8984/21/14/142203. 
  25. ^ M. Rotter, M. Tegel, and D. Johrendt (2008). "Superconductivity at 38 K in the Iron Arsenide (Ba1-xKx)Fe2As2". Physical Review Letters 101 (10): 107006. Bibcode 2008PhRvL.101j7006R. doi:10.1103/PhysRevLett.101.107006. PMID 18851249. 
  26. ^ K. Sasmal et al. (2008). "Superconducting Fe-Based Compounds (A1-xSrx)Fe2As2 with A=K and Cs with Transition Temperatures up to 37 K". Physical Review Letters 101 (10): 107007. Bibcode 2008PhRvL.101j7007S. doi:10.1103/PhysRevLett.101.107007. PMID 18851250. 
  27. ^ M. J. Pitcher et al. (2008). "Structure and superconductivity of LiFeAs". Chemical Communications 2008 (45): 5918–5920. doi:10.1039/b813153h. PMID 19030538. 
  28. ^ J. H. Tapp et al. (2008). "LiFeAs: An intrinsic FeAs-based superconductor with Tc=18 K". Physical Review B 78 (6): 060505. Bibcode 2008PhRvB..78f0505T. doi:10.1103/PhysRevB.78.060505. 
  29. ^ D. R. Parker et al. (2009). "Structure, antiferromagnetism and superconductivity of the layered iron arsenide NaFeAs". Chemical Communications (16): 2189–2191. doi:10.1039/b818911k. PMID 19360189. 
  30. ^ F.-C. Hsu et al. (2008). "Superconductivity in the PbO-type structure α-FeSe". Proceedings of the National Academy of Science 105 (38): 14262–14264. Bibcode 2008PNAS..10514262H. doi:10.1073/pnas.0807325105. PMC 2531064. PMID 18776050. http://www.pubmedcentral.nih.gov/articlerender.fcgi?tool=pmcentrez&artid=2531064. 
  31. ^ C.-H. Lee et al. (2008). "Effect of Structural Parameters on Superconductivity in Fluorine-Free LnFeAsO1-y (Ln = La, Nd)". Journal of the Physical Society of Japan 77 (8): 083704. Bibcode 2008JPSJ...77h3704L. doi:10.1143/JPSJ.77.083704. 
  32. ^ A. F. Hebard et al. (1991). "Superconductivity at 18 K in potassium-doped C60". Nature 350 (6319): 600. Bibcode 1991Natur.350..600H. doi:10.1038/350600a0. 
  33. ^ A. Y. Ganin et al. (2008). "Bulk superconductivity at 38 K in a molecular system". Nature Materials 7 (5): 367–71. Bibcode 2008NatMa...7..367G. doi:10.1038/nmat2179. PMID 18425134. 
  34. ^ N. W. Ashcroft (1968). "Metallic Hydrogen: A High-Temperature Superconductor?". Physical Review Letters 21 (26): 1748–1749. Bibcode 1968PhRvL..21.1748A. doi:10.1103/PhysRevLett.21.1748. 
  35. ^ D.C. Van der Laan, X.F. Lu, L.F. Goodrich (2011). "Compact GdBa2Cu3O7–δ coated conductor cables for electric power transmission and magnet applications". Superconductor Science and Technology 24 (4): 042001. doi:10.1088/0953-2048/24/4/042001. 
  36. ^ P. Monthoux, A. V. Balatsky, and D. Pines (1992). "Weak-coupling theory of high-temperature superconductivity in the antiferromagnetically correlated copper oxides". Physical Review B 46 (22): 14803–14817. Bibcode 1992PhRvB..4614803M. doi:10.1103/PhysRevB.46.14803. 
  37. ^ S. Chakravarthy, A. Sudbø, P. W. Anderson, S. Strong (1993). "Interlayer Tunneling and Gap Anisotropy in High-Temperature Superconductors". Science 261 (5119): 337–340. Bibcode 1993Sci...261..337C. doi:10.1126/science.261.5119.337. PMID 17836845. 
  38. ^ V. B. Geshkenbein, A. I. Larkin, and A. Barone (1987). "Vortices with half magnetic flux quanta in heavy-fermion superconductors". Physical Review B 36 (1): 235–238. Bibcode 1987PhRvB..36..235G. doi:10.1103/PhysRevB.36.235. 
  39. ^ J. R. Kirtley et al. (1995). "Symmetry of the order parameter in the high-Tc superconductor YBa2Cu3O7-δ". Nature 373 (6511): 225–228. Bibcode 1995Natur.373..225K. doi:10.1038/373225a0. 
  40. ^ J. R. Kirtley et al. (2006). "Angle-resolved phase-sensitive determination of the in-plane gap symmetry in YBa2Cu3O7-δ". Nature Physics 2 (3): 190–194. Bibcode 2006NatPh...2..190K. doi:10.1038/nphys215. 
  41. ^ C. C. Tsuei et al. (1997). "Pure dx2-y2 order-parameter symmetry in the tetragonal superconductor Tl2Ba2CuO6+δ". Nature 387 (6632): 481. Bibcode 1997Natur.387..481T. doi:10.1038/387481a0. 

External links